Influence Of Sintering Temperature On The Structure, Morphology And Bioactivity Of Bioactive Glass Powders
Authors : Ksouri Dalila . Hkireddine Hafit . Aksas Ali . Valente Tiago . Bir Fatima . Slimani Nadir . Domingos Santos José .
Abstract
In this work, a ternary bioactive glass powders (SiO2-CaO-P2O5) were prepared via sol-gel method. Initially, the bioactive glass (BG) powder was synthesized by heating the solution of precursors in ethanol at 60oC and dried at 130oC. In the other hand, the influence of the sintering temperature of the final products on the structure, morphology and bioactivity of bioactive glass powders were also investigated. After the synthesis of bioactive glass powders, the bioactivity test was confirmed and their structure and morphology were distinguished by different analyses methods. The X-ray diffraction (XRD) and SEM-EDS analysis showed the amorphous structure at low sintering temperature and a crystalline structure by increasing the sintering temperature. The bioactive glass powders obtained were bioactive and the formation of an apatite layer on their surface after immersion in SBF solution for 1, 3 and 7 days was improved by X-ray diffraction and SEM – EDS analysis.
Keywords
Biomaterials, Bioactive glasses, sol-gel methods, bioactivity.
Les articles similaires
Yahia Zeghoudi
.
pages 74-88.
Ksouri Dalila
.
pages 30-37.
بوسالم أحلام
.
عابد يوسف
.
ص 117-132.
Ksouri Dalila
.
pages 11-15.
Said Houari Amel
.
pages 257-268.