ENP Engineering Science Journal
Volume 2, Numéro 1, Pages 63-69
2022-07-29
Authors : Sebbane Yasmina . Boubakeur Ahmed . Mekhaldi Abdelouahab .
The carried out investigations aim at clarifying the correlations between physico-chemical properties and the variation of dielectric losses of Cross-Linked Polyethylene (XLPE) as Medium Voltage cable insulation during thermal aging. The used cables were manufactured by ELSEWEDY CABLES. They have been installed in Algeria where they must resist high temperatures that could exceed 50 degrees in the south of the country. For this aim, thermal aging measurements were performed on XLPE cables samples at 80, 100 and 140 °C for aging time of 5000 hours. The chemical properties were evaluated through Fourier Transform Infrared Spectrum (FTIR). In addition, the effect of aging on the crystallinity ratio, the lamellar thickness and the melting peak temperature was assessed using Differential Scanning Calorimetry (DSC). Frequency domain dielectric spectroscopy has been conducted on the aged XLPE cables in order to study the evolution of the dielectric losses. The obtained results showed that the principal aging mechanism is thermal oxidation which heads to deteriorate the morphology and increase both the polarization and losses, principally at low frequencies. It has been found that the color changes caused by the chains scission indicate the increase of interfaces between the cable insulating and semi-conductive layers, which could head to increase the dielectric losses due to the interfacial polarization.
Cross-linked Polyethylene, Cristallinity, Thermal aging, Dielectric losses
Bouajila Khedija
.
Ben Jeddi Faysal
.
pages 18-31.
Nili Mohamed Seghir
.
Nili Mohamed Seghir
.
pages 54-61.
Araissia Hanene
.
Guellati Ouanassa
.
Abbaci Fatima
.
Harat Aicha
.
El-haskouri Jamal
.
Begin Dominique
.
Guerioune Mohamed
.
Nait-merzoug Assia
.
pages 35-41.
Djelamda Sara
.
Djefaflia Fahima
.
Harat Aicha
.
Nait-merzoug Assia
.
Momodu Dami
.
Manyala Ncholu
.
Guerioune Mohamed
.
Guellati Ouanassa
.
pages 42-47.
موساوي جمال
.
بوخنوف أرزقي
.
ص 421-441.